Preparation and mechanical properties of polypropylene fiber reinforced calcined kaolin-fly ash based geopolymer

张祖华  姚晓  诸华军  华苏东  陈悦  
【摘要】:To improve the environmental benefits and solve the problems of large shrinkage and high brittleness, the partial replacement of calcined kaolin by fly ash as a raw material for geopolymer synthesis and the influences of polypropylene (PP) fiber on the mechanical properties and volume stability were investigated. The results show that compressive strength of the geopolymer containing 33.3%(mass fraction) fly ash by steam curing at 80 ℃ for 6 d is improved by 35.5%. The 3-day compressive strength, flexural strength and impacting energy of geopolymers containing 0.05%PP fiber increase by 67.8%, 36.1% and 6.25%, while the shrinkage and modulus of compressibility decrease by 38.6% and 31.3%, respectively. The results of scanning electron microscopy (SEM) and the appearances of crack growths confirm that PP fiber can offer a bridging effect over the harmful pores and defects and change the expanding ways of cracks, resulting in a great improvement of strength and toughness.

知网文化
 快捷付款方式  订购知网充值卡  订购热线  帮助中心
  • 400-819-9993
  • 010-62982499
  • 010-62783978