多孔TiO_2包覆的磁性核-壳纳米复合材料:制备和增强的光催化性能(英文)

刘鸿飞  季生福  郑园园  李明  杨浩  
【摘要】:The core-shell structured TiO2/SiO2 @Fe3O4 photocatalysts were prepared using Fe3O4 as magnetic core,tetraethoxysilane(TEOS) as silica source and tetrabutyl titanate(TBOT) as titanium sources.The as-obtained structure was composed of a SiO2@Fe3O4 core and a porous TiO2 shell.The diameter of SiO2@Fe3O4 core was about 205 nm with thickness of porous TiO2 of about 5-6 nm.The 9%TiO2/6%SiO2@Fe3O4 microspheres possess the highest BET surface area and the BJH pore volume,which are 373.5 m2.g-1 and 0.28 cm3.g-1,respectively.The 9%TiO2/6%SiO2@Fe3O4 photocatalyst exhibited an excellent performance for the degradation of methyl orange and methylene blue dyes.Two different dyes were completely decolorized in 60 min under UV irradiation.The photocatalytic activity and the amount of catalyst were almost not decrease after recycling for 6 times by using external magnetic field.

知网文化
 快捷付款方式  订购知网充值卡  订购热线  帮助中心
  • 400-819-9993
  • 010-62982499
  • 010-62783978