Effect of Au film pre-deposited at different durations as inner electrode on the electrical properties and interface microstructures of Na_2O-PbO-Nb_2O_5-SiO_2 multi-layer glass-ceramic capacitors

【摘要】:To further study the effect of sputtered Au film as transition electrode layer on the electrical properties and interface microstructures of Na 2 O-PbO-Nb 2 O 5 -SiO 2 multilayer glass-ceramic capacitors, Au films pre-deposited at different time were prepared by DC magnetron sputtering. Compared with the single paste electrode structure, samples with Au films pre-deposited from 6 to 18 min have the consistent performance to effectively improve the electrical properties of the capacitors, resulting in the doubled breakdown strength, an increase of equivalent capacitance by 22% and a decrease of leakage current by an order of magnitude. SEM observations indicate that the Au films with deposition time from 6 to 18 min would all help the formation of a dense electrode/dielectric interface and inhibit the diffusion of Ag. The results reveal that Au film pre-deposited for 6 min as inner electrode was sufficient to improve the interface microstructure and therefore to inhibit the Ag diffusion and enhance the overall performance of the multi-layer glass-ceramic capacitors.

知网文化
中国知网广告投放
 快捷付款方式  订购知网充值卡  订购热线  帮助中心
  • 400-819-9993
  • 010-62982499
  • 010-62783978