| | | | | Synthesis of ZrO_2-SiC Composite by Carbothermal Reduction of Zircon | | | Zircon (mesh size≤44μm) and carbon black (mesh size≤30μm) were used as the starting materials, weighed with m(zircon) ∶m(carbon black) of 100 ∶20 and mixed fully. The specimens with the diameter of 20mm and length of 5mm were prepared by pressing at 100 MPa, then dried at 120℃ for 12h, put into a furnace with 1.5L·min-1 argon gas and fired at 1450℃, 1500℃, 1550℃, 1600℃ and 1650℃ for 4h, respectively. The chemical composition, phase composition and microstructure of the specimens were studied by chemical analysis, X-ray diffraction and scanning electronic microscope, and the carbothermal reduction reaction process was discussed by thermodynamic analysis. The results showed that the ZrO2-SiC composite could be synthesized by carbothermal reduction reaction using zircon and carbon black as the starting materials in argon atmosphere. The composite with different composition was obtained by controlling the firing temperature and partial pressure of CO gas. The proper temperature to synthesize ZrO2-SiC composite was 1600℃ in this experiment.
【分类号】：TQ175
【DOI】：CNKI:SUN:CHRF.0.2007-04-004
【正文快照】：
1 IntroductionAdding SiC whisker to the ZrO2based materials,ZrO2-SiC composite with high strength, high toughnessand good slag corrosion resistance can be prepared dueto the high toughness, good thermal shock resistanceand corrosion resistance of SiC[1]. However, the prop-erties of the ZrO2-SiC composite may often be de-creased because of non-homogeneous of ZrO2and SiCpowders during the process of preparing the composite.In addition, high price of SiC whisker increases thecosts of prod… | | |  推荐 CAJ下载  PDF下载 | | | CAJViewer7.0阅读器支持所有CNKI文件格式，AdobeReader仅支持PDF格式 | | | | Synthesis of ZrO_2-SiC Composite by Carbothermal Reduction of Zircon | | | MA Beiyue;YU JingkunSchool of Materials and Metallurgy;Northeastern University;Shenyang 110004;China | | | Zircon (mesh size≤44μm) and carbon black (mesh size≤30μm) were used as the starting materials, weighed with m(zircon) ∶m(carbon black) of 100 ∶20 and mixed fully. The specimens with the diameter of 20mm and length of 5mm were prepared by pressing at 100 MPa, then dried at 120℃ for 12h, put into a furnace with 1.5L·min-1 argon gas and fired at 1450℃, 1500℃, 1550℃, 1600℃ and 1650℃ for 4h, respectively. The chemical composition, phase composition and microstructure of the specimens were studied by chemical analysis, X-ray diffraction and scanning electronic microscope, and the carbothermal reduction reaction process was discussed by thermodynamic analysis. The results showed that the ZrO2-SiC composite could be synthesized by carbothermal reduction reaction using zircon and carbon black as the starting materials in argon atmosphere. The composite with different composition was obtained by controlling the firing temperature and partial pressure of CO gas. The proper temperature to synthesize ZrO2-SiC composite was 1600℃ in this experiment.
【Keyword】：Carbothermal reduction, Zircon, ZrO2-SiC composite |
| | | | | | 1 | 邹正光,何曾先,余石金; 天然高岭土碳热还原制备Al_2O_3/SiC复相陶瓷粉 [J]; 硅酸盐通报; 2004年04期 | | 2 | 吴宏鹏,洪彦若,孙家林; 逆反应烧结制备碳化硅/氮化硅复合材料的工艺 [J]; 硅酸盐学报; 2005年01期 | | 3 | 邹正光,何曾先,余石金; 高岭土的精细处理及其在新材料中的应用 [J]; 桂林工学院学报; 2004年02期 | | 4 | 王朝胜,邹正光,顾涛,龙飞; 天然高岭土原位还原制备SiC_w/Al_2O_3复相陶瓷粉末 [J]; 材料工程; 2006年12期 | | 5 | 颜汉军; 石英陶瓷烧结过程中氮化硅的影响 [J]; 山东陶瓷; 2007年01期 | | 6 | 朱强,于景坤; SiC–Al_2O_3系复合耐火粉体的合成(英文) [J]; 硅酸盐学报; 2008年01期 | | 7 | 肖寿仁; 氮化物结合碳化硅耐火材料的研制及其现状 [J]; 冶金能源; 2007年01期 | | 8 | 李国栋,熊翔,黄伯云,曾玉林; TaC涂层的氧化特征与氧化机制 [J]; 中国有色金属学报; 2007年03期 |
|
|
|
