A Novel Method to Improve the Electrochemical Performance of LiMn_2O_4 Cathode Active Material by CaCO_3 Surface Coating

Halil Sahan  Hüseyin Gktepe  Saban Patat  
【摘要】:Spinel LiMn2O4 was synthesized by glycine-nitrate method and coated with CaCO3 in order to enhance the electrochemical performance at room temperature (250C) and 550C. The uncoated and CaCO3-coated LiMn2O4 materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical tests. XRD and SEM results indicated that CaCO3 particles encapsulated the surface of the LiMn2O4 without causing any structural change. The charge-discharge tests showed that the specific discharge capacity fade of pristine electrode at 25 and 550C were 25.5% and 52%, respectively. However, surface modified cathode shows 7.4% and 29.5% loss compared to initial specific discharge capacity at 70th cycle for 25 and 550C, respectively. The improvement of electrochemical performance is attributed to suppression of Mn2+ dissolution into electrolyte via CaCO3 layer.
【作者单位】Deparment
【基金】:supported by the Erciyes University Research Found under the code of FBA-08-439
【分类号】:TG174.4

中国知网广告投放
 快捷付款方式  订购知网充值卡  订购热线  帮助中心
  • 400-819-9993
  • 010-62791813
  • 010-62985026