Formation of AlN from Secondary Al Resources

M.Bahgat  M.Radwan  F.E.Farghaly  
【摘要】:正Synthesis of AlN by NH4Cl-assisted direct nitridation of secondary Al resources was studied. Aluminum alloy scrap contained Mg and Zn element was used. Milled Al scrap (-1 mm) was mixed with NH4Cl and heated at 1000℃for 1 h in presence of 1 L/min N2 flow gas. The nitrided product was evaluated by X-ray diffraction semi-quantitative analysis and scanning electron microscopy (SEM). Aluminium nitride of 90.5% concentration was obtained with a hexagonal crystalline form. AlN is mostly formed in nano-whisker morphology (50-150 nm) which is homogenously distributed.
【作者单位】Central
【分类号】:TG115

【同被引文献】
中国期刊全文数据库 前10条
1 马红旭,李友国;硅钢中析出物的尺寸分布以及体积分数的测定[J];材料科学与工程;2002年03期
2 周德光,傅杰,金勇,柳得橹,康永林,王中丙,陈贵江,李烈军;CSP薄板坯的铸态组织特征研究[J];钢铁;2003年08期
3 刘光穆,郑柏平,焦国华;薄板坯与厚板坯生产电工钢的比较与分析[J];钢铁;2004年10期
4 徐匡迪;刘清友;;薄板坯流程连铸连轧过程中的细晶化现象分析[J];钢铁;2005年12期
5 张正贵;祝晓波;刘沿东;李炳南;王福;;无取向硅钢热轧板的织构[J];钢铁;2007年06期
6 仇圣桃;项利;岳尔斌;赵沛;;薄板坯连铸连轧流程生产取向硅钢技术分析[J];钢铁;2008年09期
7 李劲东,顾毓沁,过增元;降低取向硅钢片铁损的激光加工工艺研究[J];钢铁;1994年08期
8 熊星云,崔崑;降低取向硅钢板坯烧损的研究[J];钢铁;1996年09期
9 方建成,王续跃,苑鸿,于俊玲;激光照射对不同厚度硅钢片铁损的影响[J];钢铁;1999年01期
10 王小燕;刘学华;姚静;;薄板坯连铸连轧生产电工钢现状及其优势[J];钢铁研究;2006年03期
【二级引证文献】
中国硕士学位论文全文数据库 前1条
1 齐海峰;冷轧电工钢的产品质量控制[D];辽宁科技大学;2012年
中国知网广告投放
 快捷付款方式  订购知网充值卡  订购热线  帮助中心
  • 400-819-9993
  • 010-62791813
  • 010-62985026